Wheaton 800® Glass is a superior soda-lime clear glass that meets requirements for Type III soda lime glass as specified in the current Revision of the U.S. Pharmacopeia.
| Wheaton 800®: Soda Lime Glass Tubing | ||
|---|---|---|
| Glass Code: Wheaton 800® | 800 |
|
| Type | Soda Lime |
|
| Color | Clear |
|
| Principal Use | Disposavle Lab Ware |
|
Thermal Expansion Multiply by 10-7cm/cm/°C |
0 - 300°C |
88.0 |
25°C to Setting Point |
||
Thermal Shock Resistance (15 x 15cm Annealed Plates) This data is Approximately. |
3.2mm Thick°C |
|
6.4mm Thick°C |
||
12.7mm Thick°C |
||
| Thermal Stress Resistance °C | ||
Viscosity Data (This data is subject to normal manufacturing variations.) |
Strain Point°C |
507 |
Annealing Point°C |
546 |
|
Softening Point°C |
727 |
|
Working Point°C |
||
| Density g/cm3 | ||
| Young's Modulus (Multiply by 103Kg/mm2) | ||
| Log10 of Volume Resistivity ohm/cm | 250°C |
|
350°C |
||
Dielectric Properties (1 MHz 20°C) |
Power Factor % |
|
Dielectric Constant |
||
Loss Factor % |
||
| Refractive Index | ||
| Stress - Optical Coefficient. (nm/cm) / (Kg/mm2) | ||
| Chemical Compostion: Components in Approx. Weight % | ||||||||
|---|---|---|---|---|---|---|---|---|
| Silicon Dioxide
(SiO2) |
Boron Oxide
(B2O3) |
Aluminum Oxide
(AI2O3) |
Calcuim Oxide
(CaO) |
Magnesium Oxide
(MGO) |
Sodium Oxide
(Na2O) |
Potassium Oxide
(K20) |
Barium Oxide
(BaO) |
Iron Oxide
(Fe2O3) |
72.3% |
.3% |
2.7% |
10.3% |
.3% |
13.4% |
.5% |
.2% |
.04% |